A268 · TP409
For A268 · TP409, astm specification is A268; class or grade is TP409; esab preheat group is C; esab-recommended smaw (stick) filler is AR 309/309H/308/308H, OK 61.25; esab-recommended gmaw/gtaw filler is Autrod/Tigrod 409Nb, recorded from its source on 2026-09-16.
- ASTM specification
- A268 verified
- Class or grade
- TP409 verified
- ESAB preheat group
- C verified
- ESAB-recommended SMAW (stick) filler
- AR 309/309H/308/308H, OK 61.25 verified
- ESAB-recommended GMAW/GTAW filler
- Autrod/Tigrod 409Nb verified
- ESAB-recommended FCAW (gas-shielded flux-cored) filler
- SB 308H verified
- ESAB-recommended MCAW (metal-cored) filler
- AR MC409Ti verified
- Suggested preheat, low hydrogen (H8 and less), by thickness
- T < .75: 200, .75 < T < 1.5: 300, 1.5 < T < 2.5: 300, T > 2.5: 350 our reading
- Suggested preheat, hydrogen above H8, by thickness
- T < .75: NR, .75 < T < 1.5: NR, 1.5 < T < 2.5: NR, T > 2.5: NR our reading
Values marked our reading are our classification of what the source says — the source does not print them in those words. The quote below is the evidence for each one; judge it yourself.
What the source says
A268 TP405 C OK 68.17 Autrod/Tigrod 410NiMo TP409 C AR 309/309H/308/308H, OK 61.25 Autrod/Tigrod 409Nb
— assets.esab.com, retrieved 2026-09-16
Where each value comes from
This source states these in separate places, so each value is shown with the passage that states it.
ESAB-recommended FCAW (gas-shielded flux-cored) filler and ESAB-recommended MCAW (metal-cored) filler
SB 308H AR MC409Ti
Suggested preheat, low hydrogen (H8 and less), by thickness and Suggested preheat, hydrogen above H8, by thickness
Preheat A B C D Low Hydrogen H8 and less T < .75 70 70 200 300 .75 < T < 1.5 70 125 300 400 1.5 < T < 2.5 150 200 300 400 T > 2.5 225 300 350 500 Hydrogen > H8 T < .75 175 175 NR NR .75 < T < 1.5 225 225 NR NR 1.5 < T < 2.5 275 275 NR NR T > 2.5 300 300 NR NR
— all from assets.esab.com, retrieved 2026-09-16
Source
- assets.esab.comhttps://assets.esab.com/assetbank-esab/assetfile/22174.pdf